Werkstoffbezeichnungen nach ASTM-D 1418-76 |  | POLYMER | div. Handelsnamen (R) | | NR | Naturkautschuk |  | | IR | Isoprenkautschuk | Natsyn, Criflex IR | | SBR | Styrol-Butadien-Kautschuk | Buna Hüls,Polysar S,Soprene | | BR | Butadien-Kautschuk | Buna CB, Polybutadien K | | IIR | Butyl-Kautschuk | Polysar Butyl, Esso-Butyl | | EPDM | Ethylen-Propylendien-Kautschuk | Keltan, Buna AP, Dutral | | NBR | Acrylnitril-Butadien-Kautschuk | Perbunan, Polysar-Krynac | | CO,ECO | Epichlorhydrin-Kautschuk | Heroclor, Hydrin | | CR | Chloropren-Kautschuk | Baypren, Neoprene | | CSM | Chlorsulfonysiertes Polyethylen-Kautschuk | Hypalon | | AU,EU | Polyurethan-Kautschuk | Urepan, Adipene C | | T | Polysulfid-Kautschuk | Thiokol | | VMQ, PVMQ | Silicon-Kautschuk | Silopren | | FQ | Fluor-Silicon-Kautschuk | Silastic | | FKM | Fluorkautschuk | Viton, Fluorel, Tecnoflon | | ACM | Polyacrylat-Kautschuk | Hycar | | PUR | Polyurethan | Vulkollan | | PTFE | Polyteraflurethylen | Teflon, Hostaflon |
|
| Eigenschaften |  |  |  |  |  |  |  |  |  |  |  |  |  |  |  |  |  |  | | Zerreißfestigkeit unverstärkt | 1 | 2 | 5 | 6 | 4 | 5 | 5 | 5 | 3 | 5 | 2 | 6 | 6 | 6 | 5 | 6 | 1 | 1 | | Zerreißfestigkeit verstärkt | 1 | 2 | 2 | 4 | 3 | 3 | 2 | 3 | 2 | 3 | 1 | 5 | 4 | 4 | 3 | 3 | - | 1 | | Bruchdehnung | 1 | 1 | 2 | 3 | 2 | 3 | 2 | 3 | 2 | 3 | 2 | 4 | 4 | 4 | 3 | 3 | 2 | 1 | | Rückprallelastizität | 2 | 2 | 3 | 1 | 6 | 3 | 3 | 2 | 3 | 4 | 3 | 4 | 3 | 3 | 5 | 5 | 2 | X | | Abriebwiderstand | 2 | 2 | 2 | 1 | 3 | 3 | 2 | 3 | 2 | 3 | 1 | 5 | 5 | 5 | 4 | 4 | 1 | 3 | | Einreißfestigkeit | 2 | 2 | 3 | 5 | 3 | 3 | 3 | 3 | 2 | 4 | 3 | 4 | 6 | 6 | 3 | 4 | 1 | 2 | | elek.Durchgangswiderst. | 1 | 1 | 2 | 2 | 2 | 2 | 4 | 5 | 3 | 4 | 3 | 3 | 1 | 1 | 4 | 4 | 2 | 1 | | Temp. Ber. Heißluft + °C | 90 | 90 | 100 | 100 | 140 | 150 | 130 | 145 | 120 | 130 | 120 | 140 | 200 | 200 | 220 | 160 | 80 | 260 | | Temp. Ber. Kälte - °C | 50 | 40 | 40 | 60 | 40 | 40 | 40 | 40 | 30 | 40 | 20 | 30 | 80 | 80 | 25 | 20 | 35 | 190 | | Alterungsbeständigkeit | 3 | 3 | 3 | 3 | 2 | 1 | 3 | 2 | 2 | 2 | 2 | 3 | 1 | 1 | 1 | 2 | 1 | 1 | | Ozonbeständigkeit | 4 | 4 | 4 | 3 | 2 | 1 | 3 | 2 | 2 | 2 | 2 | 2 | 1 | 1 | 1 | 2 | 1 | 1 | | Benzinbeständigkeit | 6 | 6 | 4 | 5 | 6 | 5 | 1 | 1 | 2 | 2 | 1 | 1 | 5 | 1 | 1 | 1 | 2 | 1 | | Öl- und Fettbeständigkeit | 6 | 6 | 5 | 6 | 6 | 4 | 1 | 1 | 2 | 2 | 4 | 4 | 4 | 4 | 4 | 4 | 2 | 1 | | Säurebeständigkeit | 3 | 3 | 3 | 3 | 2 | 1 | 4 | 5 | 2 | 2 | 5 | 4 | 5 | 4 | 1 | 5 | 6 | 1 | | Alkalienbeständigkeit | 3 | 3 | 3 | 3 | 2 | 2 | 3 | 5 | 2 | 2 | 5 | 3 | 5 | 4 | 1 | 5 | 6 | 1 | | Heißes Wasser | 3 | 3 | 2 | 3 | 1 | 2 | 3 | 4 | 3 | 3 | 5 | 3 | 5 | 4 | 2 | 5 | 6 | 1 |
|
| LEGENDE: | | 1=ausgezeichnet | 2=sehr gut | 3=gut | 4=mäßig | 5=gering | 6=ungenügend | x=mit Elastomeren kein Vergleich |
|
|
|
Werkstoffbezeichnungen